GENERAL		DESCRIPTION
Available in		Rods / Tubes / Plates / Machined parts
Filler Content (Nominal Value)		25% Carbon filled
PHYSICAL	@ CONDITION		TEST METHOD	IMPERIAL			METRIC
Density			ASTM D792	0.051		lbs/in³	1.42		g/cm³
Moisture Absorption	@ 23°C, 24hrs		ASTM D570	0.4		%	0.4		%
Hardness, Shore D			ASTM D2240	98			98
MECHANICAL	@ CONDITION		TEST METHOD	IMPERIAL			METRIC
Tensile Strength			ASTM D638	32		kpsi	220		MPa
Tensile Modulus			ASTM D638	1.74		Mpsi	12		GPa
Tensile Elongation	@ break		ASTM D638	2.5		%	2.5		%
Flexural Strength			ASTM D790	42		kpsi	290		MPa
Flexural Modulus			ASTM D790	1.9		Mpsi	13		GPa
Compressive Strength			ASTM D695	65		kpsi	450		MPa
Izod Impact, Notched	@ 1/8”		ASTM D256	0.6		ft-lb/in	0.32		J/cm
THERMAL	@ CONDITION		TEST METHOD	IMPERIAL			METRIC
Glass Transition Temperature			DSC	801		°F	427		°C
HDT	@ 1.8 MPa (264 psi) @ 0.46 Mpa (66 psi)		ASTM D648	842		°F	450		°C
CTE, linear	@ 24 - 149°C		ASTM D696	6.7		μin/in-°F	12		μm/m-°C
Flammability	@ 3mm (1/8 in)		UL 94	V-0		class	V-0		class
ELECTRICAL	@ CONDITION		TEST METHOD	IMPERIAL			METRIC
Surface Resistivity*			ASTM D257	101-103		ohm/sq	101-103		ohm/sq

*Resistivity measured for PBI product is for reference only due to sensitivity to moisture and measurement protocol. Statimax 800 series are composition based grades.
This information and all further technical advice are based Polymics’ present knowledge and experience. However, neither Polymics Ltd nor any of its affiliates makes any warranty, express or implied, including merchantability or fitness for use, or accepts any liability in connection with this information or its use. This information is for use by technically skilled persons at their own discretion and risk and does not relate to the use of this product in combination with any other substance or any other process. This is not a license under any patent or other proprietary right. The use of this product resides on the determination of the customer not Polymics Ltd. The customer must determine suitability of any information or material for any contemplated use, the manner of use and whether any patents are infringed. This information gives typical properties only and is not to be used for specification purposes. Polymics reserves the right to make additions, deletions, or modifications to the information at any time without prior notification.